SAC水泥混凝土氯离子固化及钢筋锈蚀实验配合比.docx

SAC水泥混凝土氯离子固化及钢筋锈蚀实验配合比表1掺矿物掺和料配合比编号掺量水泥(kgm3)水海砂石子减水剂缓凝剂0368(OPC)18464012423.681.104对照组0368(SAC)18464012423.681.10436.8(10%)362.5(SAC)18263012233.621.09粉煤灰73.6(20%)357(SAC)17962012043.021.08110.4(30%)351.517661011852.421.06偏向岭土36.8(10%)362.5(SAC)18263012233.621.0973.6(20%)357(SAC)17962012043.021.081600目110.4(30%)351.517661011852.421.0636.8(10%)362.5(SAC)18263012233.621.09硅灰73.6(20%)357(SAC)17962012043.021.08110.4(30%)351.517661011852.421.06表2改变水泥用量和水灰比配合比水泥编号水灰比(kgm3)水海砂石子减水剂缓凝剂0.5368(OPC)18464012423.681.104对照组0.5368(SAC)18464012423.681.1040.4368(SAC)18464012423.681.104水灰比0.3368(SAC)18464012423.681.1040.5408(OPC)204619.51202.53.561.090.5368(SAC)18464012423.681.104水泥用量0.5328(SAC)164660.41281.53.81.140.5288(SAC)144680.713214.041.17表3掺阻锈剂配合比编号掺量水泥(kgm3)水海砂石子减水剂缓凝剂0368(OPC)18464012423.681.104对照组0368(SAC)18464012423.681.1041%367.4(SAC)183.76391240.13.671.104三乙醇胺2%366.9(SAC)183.4638.11238.33.671.1043%366.3(SAC)183.2637.11236.43.661.1041%367.4(SAC)183.76401240.13.671.104亚硝酸锂2%366.9(SAC)183.46401238.33.671.1043%366.3(SAC)183.26401236.43.661.104氨甲基丙醇1%367.4(SAC)183.76401240.13.671.1042%366.9(SAC)183.46401238.33.671.1043%366.3(SAC)183.26401236.43.661.104三乙醇胺l%+10%361.9(0PC)181629.41221.43.621.09+偏高岭2%+20%355.8(SAC)177.9618.81200.83.561.07±3%+30%349.7(SAC)174.8608.11180.23.501.05一、试验方法1.电化学阻抗谱采用电化学阻抗谱的方法可以对混凝土中钢筋锈蚀的速率、钢筋表面钝化膜的情况得到定量的测量。钢筋在表面的钝化膜破坏时，腐蚀电流会发生较大的变化，腐蚀电流的变化可以通过电化学测试手段获得。实验采用课题组的电化学工作站获得。交流阻抗谱的频率范围选择从IOMHZ到100kHz,扰动信号为IOmVo混凝土采用100XlOOXlOOmm的试件，每个配合比成型3个试件，测量时取3个试件的平均值。试件成型24小时候拆模，进行编号。将试件放入标准养护间养护。测试时，获取各配合比时间的交流阻抗谱图（NyqUiSt图即复数平面图），利用课题组CS电化学工作站中自带的ZVieW软件对测得的NyqUiSt图进行分析,获得曲线的拟合电路，即得到极化电阻R”再利用Stem-Geary方程式便可获得腐蚀电流密度。在实验中，试块做好后，标准养护3天开始用交流阻抗谱方法测数据，测试前为使混凝土保持湿润，用氢氧化钙溶液对其进行浸泡24小时，之后利用Corretest系统进行试验。在NyqUiSt图中弧线半径减少时，意味着腐蚀电流密度逐渐增大。低频区和高频区交界位置向左向右变化时，高频弧线与低频弧区交点的位置可以反映出物质通过混凝土传到钢筋表面的阻力，从而可以推断出混凝土内部的水化反应进行的情况。根据NyqUiSt图中容抗弧，可以判断出钢筋在混凝土中腐蚀的过程:一部分出现双容抗弧时是由电荷转移控制，另一部分是出现了Warbrug弧段时是由混凝土中溶液的扩散过程控制。